Model No.: A213

A213 Alloy Steel boiler tube

SA-213/SA-213M Specification for seamless Ferritic Alloy steel boiler, Superheater and heat exchanger tubes

Delivery Condition: Normalized and Tempered
Inspections and Tests Performed: Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength, Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, No-destructive Test, Hydrostatic Test.
Surface treatment: Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting

Inner packing: Caps on two ends of every pipe

Package: bare packing/bundle packing/wooden carton packing.

Size Tolerance
Tube Kinds	SA213 OD(D)		SA213 Thickness(S)
	OD(mm)	OD Tolerance(mm)	OD(mm)	Thickness Tolerance(mm)
Hot Rolled	=101.6	+0.4~-0.8	76~168.3	+28%~0
	>101.6~168.3	+0.4~-1.2
Cold Drawn	<25.4	0.1	=38.1	+20%~0
	25.4~38.1	0.15
	>38.1~<50.8	0.2	>38.1	+22%~0
	50.8~<63.5	0.25
	63.5~<76.2	0.3
	76.2~101.6	0.38
	>101.6~190.5	+0.38~-0.64
	>190.5~228.6	+0.38~-1.14

Grade	Tensile Strength,Min., ksi[MPa]	Yield Strength,Min., ksi[MPa]	Elongation in 2 in. or 50 mm,Min., %[Note (1),(2)]
T12	60 [415]	32 [220]	30
T23	74 [510]	58 [400]	20
T91	85 [585]	60 [415]	20
T92	90 [620]	64 [440]	20
T122	90 [620]	58 [400]	20
18Cr-2Mo	60 [415]	40 [275]	20

NOTES:

(1) When standard round 2 in. or 50 mm gage length or smaller proportionally sized specimens with gage length equal to 4D (4 times the diameter) is used, the minimum elongation shall be 22% for all ferritic grades except 18Cr-2Mo, T23 and T91.

(2) For longitudinal strip tests, a deduction from the basic minimum

CHEMICAL REQUIREMENTS FOR FERRITIC STEEL
Composition, %
Grade	Carbon	Manganese	Phosphorus, Max.	Sulfur, Max	Silicon	Chromium	Molybdenum	Titanium	Vanadium,Min.	Other Elements
T2 [Note (1)]	0.10~0.20	0.30~0.61	0.025	0.025	0.10~0.30	0.50~0.81	0.44~0.65	. . .	. . .
T5	0.15 max.	0.30~0.60	0.025	0.025	0.50 max.	4.00~6.00	0.45~0.65	. . .	. . .
T5b	0.15 max.	0.30~0.60	0.025	0.025	1.00~2.00	4.00~6.00	0.45~0.65	. . .	. . .
T5c	0.12 max.	0.30~0.60	0.025	0.025	0.50 max.	4.00~6.00	0.45~0.65	[Note (1)]	. . .
T9	0.15 max.	0.30~0.60	0.025	0.025	0.25~1.00	8.00~10.00	0.90~1.10	. . .	. . .
T11	0.05 min.~0.15 max.	0.30~0.60	0.025	0.025	0.50~1.00	1.00~1.50	0.44~0.65	. . .	. . .
T12 [Note (1)]	0.05 min.~0.15 max.	0.30~0.61	0.025	0.025	0.50 max.	0.80~1.25	0.44~0.65	. . .	. . .
T17	0.15~0.25	0.30~0.61	0.025	0.025	0.15~0.35	0.80~1.25	. . .	. . .	0.15
T21	0.05 min.~0.15 max.	0.30~0.60	0.025	0.025	0.50 max.	2.65~3.35	0.80~1.06	. . .	. . .
T22	0.05 min.~0.15 max.	0.30~0.60	0.025	0.025	0.50 max.	1.90~2.60	0.87~1.13	. . .	. . .
T23	0.04~0.10	0.10~0.60	0.03	0.01	0.50 max.	1.90~2.60	0.05~0.30	. . .	0.20~0.30	W 1.45~1.75 Cb 0.02~0.08 B 0.0005~0.006 N 0.030 max. Al 0.030 max.
T91	0.08~0.12	0.30~0.60	0.02	0.01	0.20~0.50	8.00~9.50	0.85~1.05	. . .	0.18~0.25	Cb 0.06~0.1 N 0.030~0.070 Ni 0.40 max. Al 0.04 max.
T92	0.07~0.13	0.30~0.60	0.02	0.01	0.50 max.	8.50~9.50	0.30~0.60	. . .	0.15~0.25	W 1.5~2.00 Cb 0.04~0.09 B 0.001~0.006 N 0.03~0.07 Ni 0.40 max. Al 0.04 max.
T122	0.07~0.14	0.70 max.	0.02	0.01	0.50 max.	10.00~12.50	0.25~0.60	. . .	0.15~0.30	W 1.50~2.50 Cu 0.30~1.70 Cb 0.04~0.10 B 0.0005~0.005 N 0.040~0.100 Ni 0.50 max. Al 0.040 max.
18Cr-2Mo	0.025 max.	1.00 max.	0.04	0.03	1.00 max.	17.5~19.5	1.75~2.50	[Note (3)]	. . .	N max. 0.035 Ni + Cu max. 1